Devcon® 19770

Devcon® FasMetal™ 10 HVAC Repair Kit, 2-Component, Tube, 6.5 oz, Epoxy Base, Composition: Part A: Bisphenol A Diglycidyl Ether Resin , Aluminum Flake, Calcium Carbonate, Synthetic Amorphous Silica, Crystalline Silica; Part B: Barium Sulfate, Polyamide of Tall-Oil Fatty Acid Dimers and Tetraethylenepentamine, Tris-2,4,6-(Dimethylaminomethyl)Phenol, Dimer/TOFA, Reaction Products with TETA, Calcium Carbonate, Kaolin, Triethylenetetramine, Synthetic Amorphous Silica, Crystalline Silica, Tetraethylenepentamine, Paste, 16 hr Curing, Gray/White, Slight Part A, Mild Ammonia Part B, 250 deg F, 1.64 Specific Gravity, >200 deg F Flash, Neutral Part A/10 to 11 Part B pH, 1:1 Mixing, Applicable Materials: Aluminum and Other Metal, Ceramic, Wood, Concrete and Glass, 2500 psi Tensile

Composition: Part A: Bisphenol A Diglycidyl Ether Resin , Aluminum Flake, Calcium Carbonate, Synthetic Amorphous Silica, Crystalline Silica; Part B: Barium Sulfate, Polyamide of Tall-Oil Fatty Acid Dimers and Tetraethylenepentamine, Tris-2,4,6-(Dimethylaminomethyl)Phenol, Dimer/TOFA, Reaction Products with TETA, Calcium Carbonate, Kaolin, Triethylenetetramine, Synthetic Amorphous Silica, Crystalline Silica, Tetraethylenepentamine

• Type 2-Component
• Container Type Tube
• Container Size 6.5 oz
• Base Type Epoxy
• Curing Time 16 hr
• Color Gray/White
• Temperature Range 250 deg F
• Mixing Ratio 1:1
• For Use On Aluminum and Other Metal, Ceramic, Wood, Concrete and Glass
• Flash Point >200 deg F
• Form Paste
• Odor/Scent Slight Part A, Mild Ammonia Part B
• Specific Gravity 1.64
• pH Range Neutral Part A/10 to 11 Part B

• Repairs coils in compressors
• Hardens to a rigid bond that can be ground, drilled or tapped
• Fills voids or porosity in aluminum castings
• Cured 7 days at 75 deg F
• Recoat time 10-12 hrs
• Part A: resin part B: Hardener