Loctite® 235615

Loctite® Fixmaster® Aluminum Putty, 2-Part, Series: PC 7254, Kit, 1 lb, Epoxy Base, Composition: Part A: Amine Adduct, Triethylenetetramine, Aluminum, Silicon Dioxide, Substituted Piperazine, 4,4'-Isopropylidenediphenol, Aliphatic Amine, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Aluminum, Epoxy Resin, Calcium Carbonate, Treated Fumed Silica, Paste, 464 sq-cm at 6 mm THK/0.45 kg Coverage, 20 min Application, 6 hr Curing, Silver Part A/Gray Part B, Part A: Slight/Ammoniacal, Part B: Slight, 20 to 200 deg F, Part A: 1.5/Part B: 1.5634 Specific Gravity, Part A: > 93.4 deg C/Part B: 149 deg C Flash, 4:1 By Volume/6.3:1 By Weight Mixing,

Composition: Part A: Amine Adduct, Triethylenetetramine, Aluminum, Silicon Dioxide, Substituted Piperazine, 4,4'-Isopropylidenediphenol, Aliphatic Amine, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Aluminum, Epoxy Resin, Calcium Carbonate, Treated Fumed Silica

• Type 2-Part
• Series PC 7254
• Container Type Kit
• Container Size 1 lb
• Base Type Epoxy
• Form Paste
• Coverage 464 sq-cm at 6 mm THK/0.45 kg
• Application Time 20 min
• Curing Time 6 hr
• Color Silver Part A/Gray Part B
• Odor/Scent Part A: Slight/Ammoniacal, Part B: Slight
• Temperature Rating 20 to 200 deg F
• Specific Gravity Part A: 1.5/Part B: 1.5634
• Flash Point Part A: > 93.4 deg C/Part B: 149 deg C
• Mixing Ratio 4:1 By Volume/6.3:1 By Weight
• VOC Content <10 g/L
• Applicable Materials Aluminum Casting, Steel
• Tensile Strength 4000 psi
• Shear Strength 2015 psi

• Will not sag or shrink
• Easy to mix and use
• Rebuilds worn parts fast limits downtime
• Forms a non-rusting aluminum like finish
• Superior adhesion forms a solid bond
• Corrosion inhibiting, trowelable
• D 87 shore hardness
• 60 to 80 min gel time 25 deg C
• Epoxy hardener part A, epoxy resin part B