Loctite® 219292

Loctite® Fixmaster® Steel Putty, 2-Part, Series: EA 3471, Tub, 1 lb, Epoxy Base, Composition: Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenediphenol, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine, Paste, 278 sq-cm at 6 mm THK/0.45 kg Coverage, 30 min Application, 6 hr Curing, Gray/White, Part A: Slight/Musty, Part B: Ammoniacal, -30 to 105 deg C, Part A: 2.6/Part B: 1.5 Specific Gravity, >93 deg C Flash, 2.5:1 By Volume/6.25:1 By Weight Mixing,

Composition: Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenediphenol, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine

• Type 2-Part
• Series EA 3471
• Container Type Tub
• Container Size 1 lb
• Base Type Epoxy
• Form Paste
• Coverage 278 sq-cm at 6 mm THK/0.45 kg
• Application Time 30 min
• Curing Time 6 hr
• Color Gray/White
• Odor/Scent Part A: Slight/Musty, Part B: Ammoniacal
• Temperature Rating -30 to 105 deg C
• Specific Gravity Part A: 2.6/Part B: 1.5
• Flash Point >93 deg C
• Mixing Ratio 2.5:1 By Volume/6.25:1 By Weight
• VOC Content <10 g/L
• Applicable Materials Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum
• Tensile Strength 4900 psi
• Shear Strength 1395 psi

• Steel putty is a non-slumping, two-part, steel-filled putty
• Will not sag or shrink
• Rebuilds worn parts fast limits downtime
• High steel content cures to a metal-like finish
• Superior adhesion bonds well to all metal substrates
• D 85 shore hardness
• 35 to 40 gel time at 21 deg C
• Epoxy resin part A, epoxy hardener part B